PBT 5010GT-20 BK MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Bottle cap,Fitness equipment,Automotive sector,Electronic field,Electrical field
Glass fiber reinforced,15% glass fiber reinforce,High toughness
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT-20 BK |
---|---|---|---|
Stretching length | ASTM D638 | 5.5 % | |
Flexural modulus | ASTM D790 | 4.71 GPa | |
Impact strength of cantilever beam gap | 3.2mm | ASTM D256 | 96 J/m |
coefficient of friction | ASTM D1894 | 0.25 | |
bending strength | ASTM D790 | 140.2 Mpa | |
Rockwell hardness | ASTM D785 | 118 R | |
tensile strength | ASTM D638 | 94.1 Mpa |
Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT-20 BK |
---|---|---|---|
arc resistance | ASTM D495 | 125 S | |
Dielectric loss | 10,正切 | ASTM D150 | 0.02 |
dielectric constant | 10 | ASTM D150 | 28 Pf/m |
dielectric strength | ASTM D149 | 21 KV/mm | |
Volume resistivity | ASTM D257 | 10 |
other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT-20 BK |
---|---|---|---|
purpose | 20%玻纤.注塑增强级.高抗冲击.适合机械、电子、电气、汽车等租燃的工程制品。 |
physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT-20 BK |
---|---|---|---|
Shrinkage rate | 平行方向 | 0.5 % | |
filler content | 15 wt% | ||
Shrinkage rate | 垂直方向 | 1.1 % | |
Water absorption rate | 23℃,24hr | ASTM D570 | 0.09 % |
Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010GT-20 BK |
---|---|---|---|
specific heat | 0.5 | ||
Heat distortion temperature | 0.45MPa,HDT | ASTM D648 | 210 °C |
1.86Mpa,HDT | ASTM D648 | 200 °C | |
melting temperature | DSC法 | 224 °C | |
Linear coefficient of thermal expansion | 5.5 | ||
UL flame retardant rating | UL 94 | HB |