TPU A 60 E 4902 HUNTSMAN GERMANY
IROGRAN®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | HUNTSMAN GERMANY/A 60 E 4902 |
---|---|---|---|
Shore hardness | ShoreA,Injection | ASTM D2240 | 56 |
ShoreA,Injection | DIN 53505 | 55 | |
ShoreD,Injection | DIN 53505 | 15 | |
ShoreD,Injection | ASTM D2240 | 15 |
thermal performance | Test Condition | Test Method | HUNTSMAN GERMANY/A 60 E 4902 |
---|---|---|---|
Melting temperature | Internal Method | 98.9to130 °C | |
TMA | High:635.0μm | Internal Method | 145 °C |
Low:635.0μm | Internal Method | 110 °C |
mechanical properties | Test Condition | Test Method | HUNTSMAN GERMANY/A 60 E 4902 |
---|---|---|---|
Wear resistance | -- | ASTM D395 | 43 mm³ |
-- | DIN 53516 | 43 mm³ |
Physical properties | Test Condition | Test Method | HUNTSMAN GERMANY/A 60 E 4902 |
---|---|---|---|
Melt Volume Flow Rate (MVR) | 160°C/8.7kg | 35.0 cm3/10min |
elastomer | Test Condition | Test Method | HUNTSMAN GERMANY/A 60 E 4902 |
---|---|---|---|
Permanent compression deformation | 200%Strain | ASTM D412 | 8 % |
70°C,24hr | DIN 53517 | 60 % | |
23°C,70hr | DIN 53517 | 35 % | |
200%Strain | DIN 53504 | 8 % | |
23°C,70hr | ASTM D395 | 40 % | |
70°C,24hr | ASTM D395 | 80 % | |
Shore hardness | ASTM D2632 | 60 % | |
tear strength | 0.635mm | ASTM D624 | 35.9 kN/m |
0.635mm | DIN 53515 | 25 kN/m | |
Tensile strain | Break,0.635mm | DIN 53504 | 900 % |
Break,0.635mm | ASTM D412 | 720 % | |
tensile strength | 100%Strain,0.635mm | DIN 53504 | 1.40 Mpa |
Break,0.635mm | DIN 53504 | 10.0 Mpa | |
Break,0.635mm | ASTM D412 | 7.52 Mpa | |
300%Strain,0.635mm | DIN 53504 | 2.40 Mpa | |
100%Strain,0.635mm | ASTM D412 | 2.34 Mpa | |
300%Strain,0.635mm | ASTM D412 | 4.07 Mpa |