PPA A-1133 SE WH134 SOLVAY USA

AMODEL®

Phone,Vehicle electronics,Industrial components,Automotive interior parts,Shell,Industrial applications,Metal substitution,Fuel pipeline,Machine/mechanical components,Application in the automotive field,Power/Other Tools,Laptop case,Parts under the hood of a car

Filler: Glass fiber reinf,33% filler by weight,33% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	SOLVAY USA/A-1133 SE WH134
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	280 °C
Vicat softening temperature	Melting Temperature	ISO 11357-3	313 °C

flame retardant performance	Test Method	SOLVAY USA/A-1133 SE WH134
UL flame retardant rating	UL -94	HB 1.5mm
		UL -94	HB 3.0mm
		UL -94	HB 0.84mm

mechanical properties	Test Condition	Test Method	SOLVAY USA/A-1133 SE WH134
Bending modulus	23°C	ISO 178	11600 Mpa
bending strength	23°C	ISO 178	319 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.5 kJ/m²
Elongation at Break	23°C	ISO 527-2	2.5 %
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.8 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	73 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	49 kJ/m²
Tensile modulus	23°C	ISO 527-2	13400 Mpa
tensile strength	23°C	ISO 527-2	233 Mpa

Electrical performance	Test Condition	Test Method	SOLVAY USA/A-1133 SE WH134
Dielectric strength	3.20mm	IEC 60243-1	39 KV/mm
Volume resistivity		IEC 60093	1E+15 Ω.cm

Physical properties	Test Condition	Test Method	SOLVAY USA/A-1133 SE WH134
density		ISO 1183	1.48 g/cm³