Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Copolymer PROTEQ™ C4UT2 Ixom Operations Pty Ltd
--
--
Filler, talc filler, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Ixom Operations Pty Ltd/PROTEQ™ C4UT2 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 60 J/m |
| Suspended wall beam without notch impact strength | 3.20mm | ASTM D256 | 850 J/m |
| hardness | Test Condition | Test Method | Ixom Operations Pty Ltd/PROTEQ™ C4UT2 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 69 |
| 邵氏D,15秒 | ISO 868 | 64 |
| Mechanical properties | Test Condition | Test Method | Ixom Operations Pty Ltd/PROTEQ™ C4UT2 |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 100 % |
| bending strength | 3.20mm | ASTM D790 | 38.0 MPa |
| tensile strength | 3.20mm | ASTM D638 | 25.0 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 1500 MPa |
| flammability | Test Condition | Test Method | Ixom Operations Pty Ltd/PROTEQ™ C4UT2 |
|---|---|---|---|
| Hot filament ignition temperature | 1.6mm | AS/NZS60695 | 550 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Ixom Operations Pty Ltd/PROTEQ™ C4UT2 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 1.3 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| density | ASTM D792 | 0.970 g/cm³ |
| Thermal performance | Test Condition | Test Method | Ixom Operations Pty Ltd/PROTEQ™ C4UT2 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 125 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 60.0 °C |