Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO 540Z ASAHI JAPAN
XYRON™
Automotive interior parts、Automotive sector、Industrial machinery、Electronic field、Electrical field
Flame retardant、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/540Z |
|---|---|---|---|
| Water absorption rate | 23℃,50%RH,24Hr | ASTM D-570 | 0.10 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/540Z |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 69 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 179 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 6137 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | 23℃,50%RH | ASTM D-638 | 50 % |
| Tensile modulus | ASTM D638/ISO 527 | 7482 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23℃,50%RH | ASTM D-790 | 1000 kg/cm |
| elongation at break | ASTM D638/ISO 527 | 3.3 % | |
| Impact strength of cantilever beam gap | 6.4mm带切口23℃ | ASTM D-256 | 15 Kg cm/cm |
| tensile strength | ASTM D638/ISO 527 | 117 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | 23℃,50%RH | ASTM D-790 | 25000 kg/cm |
| tensile strength | 23℃,50%RH | ASTM D-638 | 700 kg/cm |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/540Z |
|---|---|---|---|
| Dielectric loss | 23℃,50%RH,10，正切 | ASTM D-150 | 0.0027 |
| dielectric strength | 短时间法2mm厚 | ASTM D-149 | 26 KV/mm |
| Surface Resistivity | ASTM D257/IEC 60093 | 0.016E15 Ω | |
| arc resistance | 钨电极 | ASTM D-495 | 70 Secretary |
| dielectric constant | ASTM D150/IEC 60250 | 3.6 | |
| Surface Resistivity | 23℃,50%RH | ASTM D-257 | 10 Ω |
| dielectric constant | 23℃,50%RH,10 | ASTM D-150 | 2.7 |
| Volume resistivity | 23℃,50%RH | ASTM D-257 | 10 Ω.cm |
| ASTM D257/IEC 60093 | 2.3e15 Ω.cm |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/540Z |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.4-1.1 % | |
| density | ASTM D792/ISO 1183 | 1.45 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/540Z |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/540Z |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 203 ℃（℉） |
| 18.6Kg/cm，HDT | ASTM D-648 | 120 °C | |
| melting temperature | 225 ℃（℉） | ||
| UL flame retardant rating | 1.6mm | UL -94 | V-0 |