POM 100 NC010 DUPONT JAPAN
Delrin®
Thin walled products、Fitness equipment
High rigidity、High hardness、Thermal stability、high viscosity、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| -30°C | ISO 179/1eU | 430 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 4.00 µgC/g |
| hardness | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 121 |
| M计秤 | ISO 2039-2 | 90 |
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2900 Mpa |
| compression stress | ISO 604 | 110 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 45 % | |
| Flexural modulus | ISO 178 | 2900 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 26 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1600 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 72.0 Mpa |
| bending strength | 3.5%应变 | ISO 178 | 79.0 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 41 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Surface Resistivity | IEC 60093 | 3E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 5.5E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO 6452 | 91 % |
| G-value(condensate) | ISO 6452 | 1E-04 g | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| burning rate | 1.00mm | ISO 3795 | 30 mm/min |
| physical property | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.90 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 2.2 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.90 % |
| MediumDensity | 1.19 g/cm³ | ||
| melt mass-flow rate | ISO 1133 | 2.3 g/10min | |
| SpecificHeatCapacity of Melt | 3000 J/kg/°C | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/100 NC010 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| melting temperature | ISO 11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| TD：-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO 11359-2 | 160 °C |
| vicat | -- | ISO 306/A50 | 175 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| vicat | -- | ISO 306/B50 | 160 °C |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO 11359-2 | 30.0 min/mm |
| TD：EffectiveThermalDiffusivity | ISO 11359-2 | 1E-07 m²/s |