PA6 HiFill® PA6 L LE MB Techmer Polymer Modifiers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 48 J/m |
| Supplementary Information | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| TPCI | 7964102 |
| hardness | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 119 |
| Electrical performance | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+13 ohms·cm | |
| dielectric strength | ASTM D149 | 18 kV/mm |
| Mechanical properties | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 70 % |
| Flexural modulus | ASTM D790 | 2830 MPa | |
| tensile strength | 屈服 | ASTM D638 | 90.3 MPa |
| bending strength | ASTM D790 | 115 MPa |
| flammability | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 2.8 % |
| density | ASTM D792 | 1.13 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.6 % |
| Thermal performance | Test Condition | Test Method | Techmer Polymer Modifiers/HiFill® PA6 L LE MB |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 76.7 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 178 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8.3E-05 cm/cm/°C |