Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV X4765B DSM HOLAND
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DSM HOLAND/X4765B |
|---|---|---|---|
| Shore hardness | 邵氏A,5秒,注塑 | ISO 868 | 65 |
| 邵氏A,5秒,挤塑 | ASTM D2240 | 62 | |
| 邵氏A,5秒,挤塑 | ISO 868 | 62 | |
| 邵氏A,5秒,注塑 | ASTM D2240 | 65 |
| Supplementary Information | Test Condition | Test Method | DSM HOLAND/X4765B |
|---|---|---|---|
| ApparentShearViscosity-Capillary,@206/s | 200°C | ISO 11443 | 210 Pa·s |
| 200°C | ASTM D3835 | 210 Pa·s |
| elastomer | Test Condition | Test Method | DSM HOLAND/X4765B |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 400 % |
| compression set | 23°C,22hr | ISO 815 | 23 % |
| 70°C,22hr | ASTM D395 | 32 % | |
| 125°C,70hr | ASTM D395 | 48 % | |
| elongation | 断裂 | ISO 37 | 400 % |
| compression set | 125°C,70hr | ISO 815 | 48 % |
| tensile strength | 断裂 | ISO 37 | 5.10 Mpa |
| 流量:断裂 | ASTM D412 | 4.90 Mpa | |
| tear strength | --2，横向流量 | ISO 34-1 | 25 kN/m |
| tensile strength | 横向流量:100%应变 | ASTM D412 | 2.30 Mpa |
| compression set | 23°C,22hr | ASTM D395 | 23 % |
| elongation | 流量:断裂 | ISO 37 | 340 % |
| tensile strength | 流量:100%应变 | ISO 37 | 2.90 Mpa |
| 流量:断裂 | ISO 37 | 4.90 Mpa | |
| compression set | 70°C,22hr | ISO 815 | 32 % |
| elongation | 流量:断裂 | ASTM D412 | 340 % |
| tear strength | -横向流量 | ASTM D624 | 25 kN/m |
| tensile strength | 断裂 | ASTM D412 | 5.10 Mpa |
| 横向流量:100%应变 | ISO 37 | 2.30 Mpa | |
| 流量:100%应变 | ASTM D412 | 2.90 Mpa |
| aging | Test Condition | Test Method | DSM HOLAND/X4765B |
|---|---|---|---|
| Tensile stress change rate | 150°C,168hr，断裂 | ASTM D573 | -24 % |
| volume change | 135°C,70hr,inIRM903Oil | ISO 1817 | 84 % |
| Change rate of hardness (Shore) in the air | 邵氏A,150°C,168hr | ASTM D573 | 1.0 |
| Change rate of tensile strength in air | 100%应变150°C,168hr，横向 | ISO 188 | 0.0 % |
| 100%应变135°C,1000hr，横向 | ISO 188 | 1.0 % | |
| Tensile stress change rate | 135°C,1000hr，断裂 | ISO 188 | -22 % |
| Change rate of tensile strength in air | 135°C,1000hr，横向 | ISO 188 | -18 % |
| 100%应变150°C,168hr，横向 | ASTM D573 | 0.0 % | |
| Tensile stress change rate | 135°C,1000hr，断裂 | ASTM D573 | -22 % |
| 150°C,168hr，断裂 | ISO 188 | -24 % | |
| Change rate of tensile strength in air | 100%应变135°C,1000hr，横向 | ASTM D573 | 1.0 % |
| Change rate of hardness (Shore) in the air | 邵氏A,135°C,1000hr | ISO 188 | 1.0 |
| 邵氏A,150°C,168hr | ISO 188 | 1.0 | |
| Change rate of tensile strength in air | 135°C,1000hr，横向 | ASTM D573 | -18 % |
| 150°C,168hr，横向 | ASTM D573 | -20 % | |
| Change rate of hardness (Shore) in the air | 邵氏A,135°C,1000hr | ASTM D573 | 1.0 |
| volume change | 135°C,70hr,inIRM903Oil | ASTM D471 | 84 % |
| Change rate of tensile strength in air | 150°C,168hr，横向 | ISO 188 | -20 % |