ABS GF10 NC010 UMG JAPAN
UMG ABS®
--
Filler: Glass fiber reinf、10% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 7.0 kJ/m² |
| -30°C | ISO 179 | 3.0 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 115 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| melt mass-flow rate | 13 g/10min |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 116 Mpa |
| Flexural modulus | 4200 Mpa | ||
| 23°C | ISO 178 | 4200 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 4800 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 83.0 Mpa |
| Charpy Notched Impact Strength | 7 KJ/m |
| flammability | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.20-0.40 % |
| density | 23°C | ISO 1183 | 1.11 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 13.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/GF10 NC010 |
|---|---|---|---|
| Heat distortion temperature | HDT | 98 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 98.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | HB |