PC/ABS C3650-111 SABIC INNOVATIVE SINGAPHORE
CYCOLOY™
Shell、Electronic and electrical
High mobility、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 48 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 13 kJ/m² |
| 23°C | ISO 180/1A | 45 kJ/m² | |
| 0°C | ISO 180/1A | 15 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 124 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 113 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.80 |
| Dissipation Factor | 50Hz | ASTM D150 | 6E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Dissipation Factor | 60Hz | ASTM D150 | 6E-03 |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.80 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Dissipation Factor | 50Hz | IEC 60250 | 4E-03 |
| 60Hz | IEC 60250 | 4E-03 | |
| 1MHz | IEC 60250 | 6E-03 | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2600 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 50.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.9 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| tensile strength | 断裂 | ASTM D638 | 51.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.5 % |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2690 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 55.0 Mpa |
| Tensile modulus | ASTM D638 | 2860 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 101 Mpa |
| elongation | 断裂 | ASTM D638 | 35 % |
| bending strength | ISO 178 | 100 Mpa | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 55 % |
| tensile strength | 屈服 | ASTM D638 | 64.8 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >50 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VB |
| 1.5mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 37 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 0.60 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 8.5 g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 8.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/C3650-111 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 102 °C |
| Linear coefficient of thermal expansion | MD：23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 100 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| vicat | ASTM D152510 | 110 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 91.0 °C |
| RTI Str | UL 746 | 60.0 °C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| vicat | -- | ISO 306/B120 | 110 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 108 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| Linear coefficient of thermal expansion | TD：23to60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 88.9 °C |
| RTI Elec | UL 746 | 60.0 °C |