Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XHT4141 NA5D001T SABIC INNOVATIVE NANSHA
LEXAN™ 
Casters,Sports Equipment
High mobility,transparent,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
163 到 167°CIEC 60695-10-2通过
Heat Deflection Temperature1.8 MPa, 未退火, 3.20 mmASTM D648165 °C
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9ISO 75-2/Af162 °C
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9ISO 75-2/Bf173 °C
0.45 MPa, 未退火, 3.20 mmASTM D648174 °C
Linear coefficient of thermal expansion横向 : -40°CISO 11359-26.0E-5 cm/cm/°C
横向 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
流动 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
RTIUL 746150 °C
RTI ElecUL 746150 °C
RTI ImpUL 746130 °C
thermal conductivity25°CASTM C1770.20 W/m/K
vicat--ASTM D152510183 °C
--ISO 306/B120181 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
bending strength屈服, 50.0 mm 跨距4ASTM D790120 Mpa
--5,6ISO 17880.0 Mpa
elongation屈服ISO 527-2/507.0 %
屈服3ASTM D6387.0 %
断裂3ASTM D63850 %
断裂ISO 527-2/5050 %
flexural modulus50.0 mm 跨距4ASTM D7902600 Mpa
--5ISO 1782600 Mpa
tensile modulus--ISO 527-2/12750 Mpa
--2ASTM D6382730 Mpa
tensile strength断裂ISO 527-2/5067.0 Mpa
断裂3ASTM D63869.0 Mpa
屈服ISO 527-2/5078.0 Mpa
屈服3ASTM D63877.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
dielectric constant100 HzASTM D1503.12
1 MHzASTM D1503.02
High arc combustion index (HAI)UL 746PLC 0
Hot wire ignition (HWI)UL 746PLC 3
surface resistivityASTM D257> 1.0E+17 ohms
volume resistivityASTM D257> 1.0E+17 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
melt mass-flow rate330°C/2.16 kgASTM D123825 g/10 min
Melt volume flow rate330°C/2.16 kgISO 113324.0 cm3/10min
shrinkage rate3.20 mm，Flow内部方法0.60 - 0.95 %
water absorption rate饱和, 23°CISO 620.50 %
平衡, 23°C, 50% RHISO 620.25 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
-30°CISO 179/1eA9.0 kJ/m²
Dart impact23°C, Total EnergyASTM D376372.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
23°CISO 180/1U无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13875 °C
Metallic haze起始内部方法175 °C
UL flame retardant rating3.0 mmUL 94HB
1.5 mmUL 94HB
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XHT4141 NA5D001T
Back pressure0.300 to 0.700 Mpa
drying temperature135 °C
drying time4.0 to 6.0 hr
Exhaust hole depth0.025 to 0.080 mm
mold temperature95 to 130 °C
Processing (melt) temperature300 to 345 °C
screw speed40 to 90 rpm
Spray nozzle temperature295 to 340 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder300 to 345 °C
Temperature at the rear of the barrel280 to 325 °C
Temperature in the middle of the barrel290 to 335 °C