ABS 3100M TAIDA TAIWAN
TAITALAC®
Footwear
High impact resistance、High rigidity、Fatigue resistance、Ultra high impact resista、High rigidity、Fatigue resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TAIDA TAIWAN/3100M |
|---|---|---|---|
| Vicat Softening Temperature | ASTMD15255 | 101 °C | |
| Heat Deflection Temperature | 1.8 MPa, 退火, 12.7 mm | ASTM D648 | 85 °C |
| Vicat Softening Temperature | ASTM D1525 | 101 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 °C |
| Hardness | Test Condition | Test Method | TAIDA TAIWAN/3100M |
|---|---|---|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 100 |
| Mechanical Properties | Test Condition | Test Method | TAIDA TAIWAN/3100M |
|---|---|---|---|
| Tensile Strength | 屈服,23°C,3.18mm | ASTMD638 | 38.6 Mpa |
| Flexural Modulus | 23℃ | ASTM D790 | 2070 Mpa |
| Tensile Strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 31.7 Mpa |
| 屈服, 23℃, 3.18 mm | ASTM D638 | 38.6 Mpa | |
| Tensile Elongation | 断裂,23°C,3.18mm | ASTMD638 | 40 % |
| Flexural Strength | 屈服,23°C | ASTMD790 | 58.6 Mpa |
| 屈服, 23℃ | ASTM D790 | 58.6 Mpa | |
| Rockwell Hardness | R 级, 23℃ | ASTM D785 | 100 |
| Tensile Elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 40 % |
| Notched Izod Impact Strength | 23℃, 3.18 mm | ASTM D256 | 360 J/m |
| Flexural Modulus | 23°C | ASTMD790 | 2070 Mpa |
| Tensile Strength | Break,23°C,3.18mm | ASTMD638 | 31.7 Mpa |
| Notched Izod Impact Strength | 23℃, 6.35 mm | ASTM D256 | 310 J/m |
| Physical | Test Condition | Test Method | TAIDA TAIWAN/3100M |
|---|---|---|---|
| Melt Mass-Flow Rate | 220℃/10.0 kg | ASTM D1238 | 6 g/10 min |
| Moisture Absorption | 饱和 | ASTM D570 | < 0.30 % |
| Density / Specific Gravity | ASTM D792 | 1.03 g/cm³ | |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 6.0 g/10min |
| Density / Specific Gravity | ASTMD792 | 1.03 g/cm³ | |
| Melt Mass-Flow Rate | 200℃/5.0 kg | ASTM D1238 | 0.6 g/10 min |
| 200°C/5.0kg | ASTMD1238 | 0.60 g/10min | |
| Modeling Shrinkage | MD | ASTM D955 | < 0.40 % |
| Moisture Absorption | 饱和 | ASTMD570 | <0.30 % |
| Modeling Shrinkage | MD | ASTMD955 | <0.40 % |
| Impact Properties | Test Condition | Test Method | TAIDA TAIWAN/3100M |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 310 J/m |
| 23°C,3.18mm | ASTMD256 | 360 J/m |