ABS 250 X10 TORAY MALAYSIA
Toyolac®
Industrial machinery、Fitness equipment
High rigidity、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY MALAYSIA/250 X10 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 115 |
| Electrical performance | Test Condition | Test Method | TORAY MALAYSIA/250 X10 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTMD150 | 6.3E-03 |
| dielectric constant | 1kHz | ASTMD150 | 3.10 |
| Surface resistivity 5 | ASTMD257 | >1.0E+16 ohms | |
| Volume resistivity | 23°C | ASTMD257 | >1.0E+16 ohms·cm |
| Dielectric strength 6 | ASTMD149 | 24 KV/mm |
| Mechanical properties | Test Condition | Test Method | TORAY MALAYSIA/250 X10 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile modulus | ISO527-2/1 | 2900 Mpa | |
| elongation | 断裂 | ASTMD638 | 15 % |
| Flexural modulus | ASTMD790 | 2480 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 49.0 Mpa |
| Bending stress | ISO178 | 83.0 Mpa | |
| Tensile strain | 断裂 | ISO527-2/50 | >10 % |
| ASTMD790 | 77.0 Mpa |
| flammability | Test Condition | Test Method | TORAY MALAYSIA/250 X10 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | TORAY MALAYSIA/250 X10 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 44 g/10min |
| Shrinkage rate | MD | ASTMD955 | 0.40to0.60 % |
| Thermal performance | Test Condition | Test Method | TORAY MALAYSIA/250 X10 |
|---|---|---|---|
| MD | ASTMD696 | 7E-05 cm/cm/°C | |
| 1.8MPa,未退火,12.7mm | ASTMD648 | 92.0 °C | |
| thermal conductivity | ASTMC177 | 0.15 W/m/K | |
| 1.8MPa,未退火 | ISO75-2/A | 83.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 87.0 °C |