SBC KIBITON® Q-Resin PB-5903 CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | CHI MEI CORPORATION/KIBITON® Q-Resin PB-5903 | |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 70.0 °C |
| tensile strength | 屈服 | ASTM D638 | 28.4 MPa |
| Flexural modulus | 4.00mm | ISO 178 | 1.4E+06 MPa |
| Shore hardness | 邵氏D | ASTM D2240 | 71 |
| vicat | -- | ISO 306/B50 | 70.0 °C |
| tensile strength | 断裂,4.00mm | ISO 527-2/50 | 19.0 MPa |
| transmissivity | ASTM D1003 | 90.5 % | |
| density | ASTM D792 | 1.02 g/cm³ | |
| Tensile strain | Yield,4.00mm | ISO 527-2/50 | 2.0 % |
| Flexural modulus | ASTM D790 | 1370 MPa | |
| tensile strength | 屈服,4.00mm | ISO 527-2/50 | 27.0 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 2.3 kJ/m² |
| vicat | -- | ISO 306/A120 | 89.0 °C |
| -- | ISO 306/B120 | 68.0 °C | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 72 kJ/m² |
| vicat | ASTM D15256 | 84.0 °C | |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 2.8 kJ/m² |
| bending strength | 4.00mm | ISO 178 | 36.0 MPa |
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 23 J/m |
| Haze ratio | ASTM D1003 | 1.5 % | |
| density | 23°C | ISO 1183 | 1.01 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 10 g/10min |
| vicat | -- | ISO 306/A50 | 93.0 °C |
| Tensile strain | 断裂,4.00mm | ISO 527-2/50 | 200 % |
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 10.0 cm³/10min |
| bending strength | ASTM D790 | 33.3 MPa | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 71.0to83.0 °C |