Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS NH1017T Samsung Cheil South Korea
INFINO®
Casters、tubing
Hydrolysis resistance、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/NH1017T
Melt mass flow rate
ASTM D1238/ISO 1133
g/10min
6
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
5
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
5
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/NH1017T
CharpyNotchedImpactStrength
23°C
ISO179/1eA
kJ/m²
1
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/50
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
5
tensile strength
屈服
ISO527-2/50
Mpa
5
tensile strength
断裂
ASTMD638
Mpa
4
tensile strength
断裂
ISO527-2/50
Mpa
4
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
elongation
断裂
ASTMD638
%
8
elongation
断裂
ISO527-2/50
%
1
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
8
Bending strength
ASTMD790
Mpa
7
bending strength
ISO178
Mpa
8
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/NH1017T
RTI Imp
2.0mm
UL746
°C
8
RTIElec
2.0mm
UL746
°C
8
RTIStr
2.0mm
UL746
°C
8
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
8
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
7
vicat softening point
ISO306/B50
°C
9
vicat softening point
ASTM D1525/ISO R306
℃（℉）
9