PA/MXD6 1035 BLK01 MITSUBISHI ENGINEERING JAPAN
RENY™
--
Filler: Glass fiber reinf、60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1035 BLK01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 80 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1035 BLK01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 24300 Mpa | |
| bending strength | ISO 178 | 447 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.6 % |
| Flexural modulus | ISO 178 | 21600 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 285 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1035 BLK01 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1035 BLK01 |
|---|---|---|---|
| Shrinkage rate | 0.26 % | ||
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 2.30 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.90 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 3.8 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1035 BLK01 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 240 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 232 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-05 cm/cm/°C |
| TD | ISO 11359-2 | 4E-05 cm/cm/°C |