PP Homopolymer T 50 Carmel Olefins Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Carmel Olefins Ltd./ T 50 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 23 J/m |
| 23°C | ISO 180 | 2.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Carmel Olefins Ltd./ T 50 |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 12 % |
| Flexural modulus | ASTM D790 | 1450 MPa | |
| tensile strength | 屈服 | ASTM D638 | 32.0 MPa |
| Flexural modulus | ISO 178 | 1400 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 12 % |
| tensile strength | 屈服 | ISO 527-2/50 | 30.0 MPa |
| physical property | Test Condition | Test Method | Carmel Olefins Ltd./ T 50 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 25 g/10min |
| 230°C/2.16kg | ISO 1133 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | Carmel Olefins Ltd./ T 50 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 97.0 °C |
| vicat | ASTM D15254 | 155 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C |
| vicat | ISO 306/A | 155 °C |