Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 30YM241 SABIC SAUDI
STAMAX®
Automotive sector,Application in the automotive field
High rigidity,high strength,Chemical coupling,heat-resisting,Filler: Long glass fiber,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC SAUDI/30YM241 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C,注塑 | ISO 179/1eU | 36 kJ/m² |
| 23°C,注塑 | ISO 179/1eU | 52 kJ/m² | |
| Dart impact | 23°C，总能量 | ISO 6603-2 | 58.0 J/cm |
| Mechanical properties | Test Condition | Test Method | SABIC SAUDI/30YM241 |
|---|---|---|---|
| Flexural modulus | 23°C,注塑 | ISO 178 | 5900 Mpa |
| tensile strength | 120°C,注塑 | ISO 527-2/1B | 51.0 Mpa |
| bending strength | 23°C,注塑 | ISO 178 | 147 Mpa |
| Tensile modulus | 120°C,注塑 | ISO 527-2/1B | 3500 Mpa |
| Flexural modulus | 80°C,注塑 | ISO 178 | 4200 Mpa |
| bending strength | 80°C,注塑 | ISO 178 | 86.0 Mpa |
| Tensile modulus | 23°C,注塑 | ISO 527-2/1B | 6650 Mpa |
| tensile strength | 23°C,注塑 | ISO 527-2/1B | 110 Mpa |
| 80°C,注塑 | ISO 527-2/1B | 70.0 Mpa | |
| Tensile modulus | 80°C,注塑 | ISO 527-2/1B | 4600 Mpa |
| Tensile strain | 断裂,23°C,注塑 | ISO 527-2/1B | 2.3 % |
| Thermal performance | Test Condition | Test Method | SABIC SAUDI/30YM241 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 5.1E-05 cm/cm/°C |
| MD：23到80°C | ASTM D696 | 4.1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 156 °C |