Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 505RU-131 SABIC INNOVATIVE SHANGHAI
LEXAN™
Home appliance products、Automotive components
Bromine free flame retard、High transparency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/505RU-131 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 73 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 25.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/505RU-131 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 60.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| tensile strength | 断裂 | ASTM D638 | 62.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3200 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 72.0 Mpa |
| Tensile modulus | ASTM D638 | 3600 Mpa | |
| elongation | 断裂 | ASTM D638 | 6.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 114 Mpa |
| ISO 178 | 122 Mpa | ||
| Flexural modulus | ISO 178 | 3500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 6.0 % |
| tensile strength | 屈服 | ASTM D638 | 74.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/505RU-131 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/505RU-131 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 3.0mm | UL 94 | 5VB5VA | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 °C |
| 1.0mm | IEC 60695-2-13 | 850 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/505RU-131 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| Outdoor applicability | UL 746C | f1 | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 7.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/505RU-131 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 149 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 8.5E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 147 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 136 °C |
| vicat | ASTM D152510 | 149 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 137 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |