PBT+ASA KumhoSunny PBT/ASA HBA5810G Shanghai KumhoSunny Plastics Co., Ltd.
--
Applications and connectors in the automotive field
Filler, glass fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PBT/ASA HBA5810G |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
| -30°C | ISO 179 | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PBT/ASA HBA5810G |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| tensile strength | ISO 527-2/5 | 75.0 MPa | |
| Flexural modulus | ISO 178 | 3800 MPa | |
| bending strength | ISO 178 | 120 MPa |
| Electrical performance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PBT/ASA HBA5810G |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| physical property | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PBT/ASA HBA5810G |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.40to0.80 % |
| density | 23°C | ISO 1183 | 1.33 g/cm³ |
| melt mass-flow rate | 265°C/2.16kg | ISO 1133 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./KumhoSunny PBT/ASA HBA5810G |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |