PA4T F11C DSM HOLAND
ForTii®
Electronic and electrical、Automotive Applications
Thermal stability、Lubricity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDSM HOLAND/F11C
Impact strength of simply supported beam without notch23°CISO 179/1eU50 kJ/m²
Mechanical propertiesTest ConditionTest MethodDSM HOLAND/F11C
tensile strength 断裂, 160°CISO 527-270.0 Mpa
Tensile modulus--ISO 527-212000 Mpa
Tensile strain断裂, 120°CISO 527-22.7 %
bending strengthISO 178245 Mpa
Tensile strain断裂ISO 527-22.0 %
Flexural modulusISO 17811500 Mpa
Tensile strain断裂, 160°CISO 527-23.7 %
tensile strength 断裂ISO 527-2155 Mpa
断裂, 120°CISO 527-2105 Mpa
Tensile modulus160°CISO 527-25500 Mpa
120°CISO 527-28000 Mpa
Electrical performanceTest ConditionTest MethodDSM HOLAND/F11C
relative permittivity100 HzIEC 602504.20
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric strengthIEC 60243-133 KV/mm
relative permittivity1.00 GHzIEC 602503.90
1 MHzIEC 602503.90
10.0 GHzIEC 602503.90
flammabilityTest ConditionTest MethodDSM HOLAND/F11C
Flammability levelUL 94V-0
physical property Test ConditionTest MethodDSM HOLAND/F11C
Water absorption rate平衡, 23°C, 50% RHISO 621.6 %
Shrinkage rate流量ISO 294-40.30 %
横向流量ISO 294-41.2 %
Thermal performanceTest ConditionTest MethodDSM HOLAND/F11C
melting temperatureISO 11357-3325 °C
Heat distortion temperature1.8 MPa, 未退火，HDTISO 75-2/A305 °C
RTI Elec0.35 mmUL 746140 °C
Linear coefficient of thermal expansion流动ASTM D6963.0E-5 cm/cm/°C
横向ASTM D6963.5E-5 cm/cm/°C