Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM KFX-1008 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical components,Laptop case
High temperature resistan,Low temperature resistanc,Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1008 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 35 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1008 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 8.6E-05 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 4.2E-05 cm/cm/°C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 164 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 165 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1008 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 2.2 % |
| bending strength | ISO 178 | 179 Mpa | |
| flexural modulus | ISO 178 | 9600 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 131 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1008 |
|---|---|---|---|
| shrinkage rate | MD | 内部方法 | 0.30-0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 3E-03 % |