Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS K-200 BK DENKA JAPAN
MALECCA
Bumper
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DENKA JAPAN/K-200 BK |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTMD256 | 200 J/m | |
| Charpy Notched Impact Strength | ISO179 | 19 kJ/m² |
| hardness | Test Condition | Test Method | DENKA JAPAN/K-200 BK |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 114 |
| R级 | ISO2039-2 | 114 |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/K-200 BK |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/50 | 39.0 Mpa |
| 屈服 | ISO527-2/50 | 48.0 Mpa | |
| Tensile modulus | ISO527-2/1 | 2500 Mpa | |
| Flexural modulus | ASTMD790 | 2350 Mpa | |
| Bending stress | ISO178 | 78.0 Mpa | |
| Tensile modulus | ASTMD638 | 41.0 Mpa | |
| Flexural modulus | ISO178 | 2450 Mpa | |
| ASTMD790 | 75.0 Mpa | ||
| Nominal tensile fracture strain | ISO527-2/50 | 28 % |
| flammability | Test Condition | Test Method | DENKA JAPAN/K-200 BK |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | DENKA JAPAN/K-200 BK |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.50to0.70 % |
| density | 23°C | ISO1183 | 1.07 g/cm³ |
| ASTMD792 | 1.06 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/K-200 BK |
|---|---|---|---|
| vicat | ISO306/B | 115 °C | |
| 1.8MPa,未退火 | ISO75-2/Af | 95.0 °C | |
| Hot deformation temperature 5 | 1.8MPa,Unannealed | ASTMD648 | 106 °C |
| vicat | ASTMD15256 | 116 °C |