PC BPL1000 BK SABIC INNOVATIVE NANSHA

LEXAN™

Automotive components,Electronic and electrical accessories,Thin walled products

UV resistance,Hydrolysis resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/BPL1000 BK
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	96.1 °C
Hot deformation temperature		0.45MPa,Unannealed,3.20mm	ASTM D648	106 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7E-05 cm/cm/°C
		TD：-40to40°C	ISO 11359-2	7E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	7E-05 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI Str		UL 746	80.0 °C
Vicat softening temperature	--	ISO 306/B120	114 °C
		--	ISO 306/B50	113 °C
			ASTM D152511	111 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/BPL1000 BK
Bending modulus	50.0mmSpan	ASTM D790	2670 Mpa
Bending modulus			ISO 178	2370 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	102 Mpa
bending strength			ISO 178	94.8 Mpa
elongation	Break	ASTM D638	96 %
elongation		Yield	ASTM D638	4.8 %
Tensile modulus		ASTM D638	2680 Mpa
Tensile modulus			ISO 527-2/1	2460 Mpa
Tensile strain	Break	ISO 527-2/50	97 %
Tensile strain		Yield	ISO 527-2/50	4.7 %
tensile strength	Yield	ASTM D638	63.4 Mpa
		Yield	ISO 527-2/50	64.8 Mpa
		Break	ISO 527-2/50	53.5 Mpa
		Break	ASTM D638	51.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/BPL1000 BK
Compared to the anti leakage trace index		IEC 60112	PLC 3
Dielectric strength	1.60mm,inOil	ASTM D149	27 KV/mm
Dissipation factor	1MHz	IEC 60250	0.010
		50Hz	IEC 60250	0.030
		60Hz	IEC 60250	0.030
Relative permittivity	60Hz	IEC 60250	3.00
		50Hz	IEC 60250	3.00
		1MHz	IEC 60250	2.90
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/BPL1000 BK
melt mass-flow rate	300°C/1.2kg	ASTM D1238	25 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	23.2 cm3/10min
Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70 %
		MD：3.20mm	Internal Method	0.50-0.70 %
		MD：--2	Internal Method	0.50-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate		Saturation,23°C	ISO 62	0.35 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/BPL1000 BK
Charpy Notched Impact Strength	23°C	ISO 179/1eA	18 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	48.6 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	12 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	18 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/BPL1000 BK
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	36 %
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800 °C
UL flame retardant rating	0.45mm	UL 94	V-2
UL flame retardant rating		0.8mm	UL 94	V-0