Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A625H BK TORAY JAPAN
Torelina®
Casters,Electrical applications,sporting goods
High temperature resistan,Glass fiber reinforced,Filler: Glass fiber reinf,45% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 36 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 122 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 130 mm |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.8 % |
| bending strength | 23°C | ISO 178 | 250 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 170 Mpa |
| Flexural modulus | 23°C | ISO 178 | 13000 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 24 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm |
| flammability | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| UL flame retardant rating | 0.36mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.85 % |
| MD:3.00mm4 | 内部方法 | 0.25 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A625H BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 3.7E-05 cm/cm/°C |