Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 9925A-NA1A0036 SABIC INNOVATIVE US
LEXAN™
Electronic and electrical、Thin walled products、Automotive sector
UV resistance、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/9925A-NA1A0036 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 123 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 135 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 124 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | ASTMD152513 | 140 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/9925A-NA1A0036 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 13 g/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/9925A-NA1A0036 |
|---|---|---|---|
| ASTMD638 | 2300 Mpa | ||
| Break | ASTMD638 | 60.0 Mpa | |
| fracture | ISO527-2/50 | 77 % | |
| Break | ASTMD638 | 83 % | |
| Yield,50.0mm Span | ASTMD790 | 91.0 Mpa | |
| yield | ISO527-2/50 | 6.0 % | |
| Yield | ASTMD638 | 6.0 % | |
| 50.0mm Span | ASTMD790 | 2150 Mpa | |
| fracture | ISO527-2/50 | 56.0 Mpa | |
| ISO178 | 95.0 Mpa | ||
| Yield | ASTMD638 | 60.0 Mpa | |
| yield | ISO527-2/50 | 62.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/9925A-NA1A0036 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 75.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 68 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/9925A-NA1A0036 |
|---|---|---|---|
| Flame Rating | 1.50mm | UL94 | V-0 |