Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 504L SD3039 CELANESE USA
--
Electrical applications
High rigidity、Weather resistance、Thermal stability、Filler: Glass fiber reinf、40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 53 kJ/m² |
| -30°C | ISO 179/1eU | 53 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 4.60 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 6.2E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 14700 Mpa | |
| bending strength | ISO 178 | 285 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 14500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 195 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.9 % |
| flammability | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 47 % |
| physical property | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.40-0.60 % |
| MD | ISO 294-4 | 0.20-0.60 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.020 % |
| MeltSpecificHeat | 内部方法 | 1500 J/kg/°C |
| Thermal performance | Test Condition | Test Method | CELANESE USA/504L SD3039 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 270 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 215 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| Glass Transition Temperature | ISO 11357-2 | 90.0 °C |