Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS NORYL™ GNF3 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL™ GNF3 resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C8 | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C8 | ISO 180/1U | 30 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 20.0 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 120 J/m |
| 23°C | ASTM D256 | 100 J/m | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 590 J/m |
| Impact strength of cantilever beam gap | 23°C8 | ISO 180/1A | 11 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ GNF3 resin |
|---|---|---|---|
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 7200 MPa |
| elongation | 断裂3 | ASTM D638 | 3.0 % |
| bending strength | --5,6 | ISO 178 | 160 MPa |
| elongation | 断裂 | ISO 527-2/50 | 2.5 % |
| Flexural modulus | --5 | ISO 178 | 6800 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 8200 MPa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 160 MPa |
| tensile strength | 断裂3 | ASTM D638 | 130 MPa |
| Tensile modulus | --2 | ASTM D638 | 8600 MPa |
| tensile strength | 断裂 | ISO 527-2/50 | 110 MPa |
| physical property | Test Condition | Test Method | SABIC/NORYL™ GNF3 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10to0.40 % |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 2.70 cm³/10min |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 3.2 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.040 % |
| 饱和,23°C | ISO 62 | 0.10 % | |
| density | ASTM D792 | 1.31 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL™ GNF3 resin |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 149 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 2.3E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 147 °C |
| vicat | -- | ASTMD152510 | 147 °C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Af | 139 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 139 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.1E-05 cm/cm/°C |
| TD:-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C |