Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC G-3110PH TEIJIN JAPAN
PANLITE®
Casters、Electrical applications
Flame retardant、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 5E-05 cm/cm/°C |
| RTIElec | 1.7mm | UL746 | 130 °C |
| RTIStr | 130 °C | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 130 °C |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 134 ℃（℉） | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 123 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 6E-05 cm/cm/°C |
| Vicat Softening Temperature | ISO306/B50 | 134 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.5 mm/mm.℃ | |
| Evolution Calendar intelligent importer | 1.7mm | UL746 | 120 °C |
| Heat Deflection Temperature | ASTM D648/ISO 75 | 123 ℃（℉） |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.40to0.60 % |
| MD:4.00mm | 0.35to0.55 % | ||
| Moisture Absorption | 23°C,24hr | ISO62 | 0.16 % |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Flexural Modulus | ISO178 | 3100 Mpa | |
| Flexural Strength | ASTM D790/ISO 178 | 110 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 5.0 % | |
| Tensile Strain | 断裂 | ISO527-2/5 | 5.0 % |
| Tensile Modulus | ISO527-2/1 | 3000 Mpa | |
| Flexural Stress | ISO178 | 110 Mpa | |
| Tensile Modulus | ASTM D638/ISO 527 | 3000 kg/cm²(MPa)[Lb/in²] | |
| Tensile Stress | 断裂 | ISO527-2/5 | 65.0 Mpa |
| Flexural Modulus | ASTM D790/ISO 178 | 3100 kg/cm²(MPa)[Lb/in²] |
| Impact Properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | 55 kJ/m² |
| Physical Properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.16 % | |
| Density | ASTM D792/ISO 1183 | 1270 | |
| Modeling Shrinkage | ASTM D955 | 0.35-0.55 % |
| Flammability | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Flame Rating | 0.40mm | UL94 | HB |
| 1.7mm | V-2 |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/G-3110PH |
|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 35 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 175 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 3.20 |
| 100Hz | 3.20 | ||
| Dissipation Factor? | 1MHz | 9E-03 | |
| 100Hz | 1E-03 |