Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 7151G-X01 TORAY SHENZHEN
Toraycon®
Automotive sector
Low warpage,low density,Filler: Glass fiber reinf,low density,Low warpage,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY SHENZHEN/7151G-X01 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.2 % |
| bending strength | 23°C | ISO 178 | 190 Mpa |
| Flexural modulus | 23°C | ISO 178 | 10000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 10000 Mpa |
| tensile strength | 屈服, 23℃ | ISO 527-2 | 130 Mpa |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 2.3 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 9.5 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 135 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY SHENZHEN/7151G-X01 |
|---|---|---|---|
| dielectric constant | 23°C,1kHz | IEC 60250 | 3.80 |
| dielectric strength | IEC 60243-1 | 16 KV/mm | |
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.010 |
| flammability | Test Condition | Test Method | TORAY SHENZHEN/7151G-X01 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY SHENZHEN/7151G-X01 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm1 | 内部方法 | 0.50 % |
| MD: 3.00 mm | 内部方法 | 0.20 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.090 % |
| Shrinkage rate | TD: 3.00 mm | 内部方法 | 0.50 % |
| MD:3.00mm2 | 内部方法 | 0.20 % |
| Thermal performance | Test Condition | Test Method | TORAY SHENZHEN/7151G-X01 |
|---|---|---|---|
| 1.8MPa, Not annealed | ISO 75-2/A | 163 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| 0.45MPa, Not annealed | ISO 75-2/B | 209 °C | |
| UL flame retardant rating | UL 94 | HB |