PC+PBT 9KF20400 I 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 9KF20400 I |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 25 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 55 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 9KF20400 I |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/5 | 55.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | >50 % |
| Tensile modulus | 23°C | ISO 527-2/5 | 2250 MPa |
| Electrical performance | Test Condition | Test Method | 4Plas/ 9KF20400 I |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| flammability | Test Condition | Test Method | 4Plas/ 9KF20400 I |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | 4Plas/ 9KF20400 I |
|---|---|---|---|
| Shrinkage rate | MD | 1.0 % | |
| water content | ISO 960 | <1000 ppm | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| Shrinkage rate | TD | 1.0 % |
| Thermal performance | Test Condition | Test Method | 4Plas/ 9KF20400 I |
|---|---|---|---|
| melting temperature | ISO 11357 | 125 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 110 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |