PARA Reny® NXG5945S Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Reny® NXG5945S
Charpy Notched Impact Strength23°CISO 17915 kJ/m²
Impact strength of simply supported beam without notch23°CISO 17990 kJ/m²
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Reny® NXG5945S
Tensile modulusISO 527-216000 MPa
tensile strength 断裂ISO 527-2208 MPa
Tensile strain断裂ISO 527-22.0 %
Flexural modulusISO 17814300 MPa
bending strengthISO 178349 MPa
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Reny® NXG5945S
Dissipation Factor100HzIEC 602505.5E-03
relative permittivity100HzIEC 602504.20
1MHzIEC 602504.10
Dissipation Factor1MHzIEC 602506.7E-03
flammabilityTest ConditionTest MethodMitsubishi Chemical Corporation/Reny® NXG5945S
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Reny® NXG5945S
Shrinkage rate0.32 %
Melt volume flow rate280°C/5.0kgISO 11338.50 cm³/10min
melt mass-flow rate280°C/5.0kgISO 113313 g/10min
Water absorption rate平衡,23°C,50%RHISO 620.73 %
densityISO 11831.52 g/cm³
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Reny® NXG5945S
melting temperatureISO 11357-3257 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A232 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-05 cm/cm/°C
TDISO 11359-25.6E-05 cm/cm/°C
Glass Transition TemperatureISO 11357-287.0 °C