Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML6413 WH7D174 SABIC INNOVATIVE NANSHA
LEXAN™
Lighting applications,Electronic and Electrical Applications,Plastic bag
High mobility,High optical masking
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 72.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 2500 Mpa |
| tensile strength | 屈服2 | ASTM D638 | 58.0 Mpa |
| elongation | 断裂2 | ASTM D638 | 100 % |
| 断裂 | ISO 527-2/50 | 100 % | |
| Flexural modulus | --4 | ISO 178 | 2350 Mpa |
| bending strength | 屈服, 50.0 mm 跨距3 | ASTM D790 | 85.0 Mpa |
| --4,5 | ISO 178 | 90.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 2250 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
| 屈服 | ISO 527-2/50 | 62.0 Mpa | |
| elongation | 屈服2 | ASTM D638 | 5.0 % |
| 屈服 | ISO 527-2/50 | 5.0 % | |
| tensile strength | 断裂2 | ASTM D638 | 55.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2350 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| Hot filament ignition temperature | 2.0 mm | IEC 60695-2-13 | 800 °C |
| 3.0 mm | IEC 60695-2-13 | 800 °C | |
| UL flame retardant rating | 2.0 mm | UL 94 | 5VB |
| 1.6 mm | UL 94 | V-0 | |
| Burning wire flammability index | 1.6 mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Melt volume flow rate | 260°C/5.0 kg | ISO 1133 | 20.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 24 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.40 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.7E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 135 °C |
| -- | ASTM D152512 | 134 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距7，HDT | ISO 75-2/Be | 125 °C |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 118 °C |
| RTI Imp | UL 746 | 100 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距7，HDT | ISO 75-2/Ae | 115 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 5.9E-5 cm/cm/°C |
| RTI | UL 746 | 100 °C | |
| RTI Elec | UL 746 | 100 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML6413 WH7D174 |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 250 to 290 °C | ||
| Temperature at the rear of the barrel | 230 to 260 °C | ||
| Processing (melt) temperature | 270 to 300 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 90 to 100 °C | ||
| Temperature at the front of the material cylinder | 260 to 300 °C | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 250 to 290 °C |