Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI EX07305 NC SABIC INNOVATIVE SHANGHAI
ULTEM™ 
Electrical and Electronic Applications,Automotive components
Glass fiber reinforced,lubrication,Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/EX07305 NC
23°CISO 180/1A7.8 kJ/m²
ISO 180/1U26 kJ/m²
ASTM D25667 J/m
ASTM D4812330 J/m
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/EX07305 NC
bending strength屈服,50.0mm跨距ASTM D790202 Mpa
fractureISO 527-2/5156 Mpa
ASTM D6383.0 %
coefficient of friction与自身-动态ASTM D3702Modified0.52
--5ISO 1787220 Mpa
Wear factorWasherASTM D3702Modified15.6 10^-10in^5-min/ft-lb-hr
fractureASTM D638157 Mpa
50.0mm spanASTM D7906420 Mpa
--1ASTM D6388630 Mpa
fractureISO 527-2/51.2 %
bending strength断裂,50.0mm跨距ASTM D790201 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/EX07305 NC
dielectric strength1.60mm,inOilASTM D14931 KV/mm
Volume resistivityASTM D2577.6E+16 ohms·cm
Surface ResistivityASTM D2572E+13 ohms
dielectric constant100kHzASTM D1503.30
Dissipation Factor100kHzASTM D1503.1E-03
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/EX07305 NC
Shrinkage rateMD内部方法0.40 %
TD内部方法0.52 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/EX07305 NC
Linear coefficient of thermal expansionTD:-40到40°CASTME8315.1E-05 cm/cm/°C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af207 °C
1.8MPa, Unanealed, 3.20mmASTM D648204 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8311.4E-05 cm/cm/°C