PA6 6MV14 FR4 K1681 A SCHULMAN USA
SCHULAMID®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 49 kJ/m² |
-30°C | ISO 179/1eU | 48 kJ/m² |
hardness | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
ball-indentation hardness | H358/30 | ISO 2039-1 | 160 Mpa |
Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
Tensile strain | 屈服 | ISO 527-2/1A/50 | 3.0 % |
Tensile modulus | ISO 527-2/1A/1 | 3800 Mpa | |
tensile strength | 屈服 | ISO 527-2/1A/50 | 70.0 Mpa |
Electrical performance | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
Hot wire ignition (HWI) | 0.38mm | UL 746 | PLC 4 |
High arc combustion index (HAI) | 0.38mm | UL 746 | PLC 0 |
Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 4 |
1.5mm | UL 746 | PLC 2 | |
High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 0 |
High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
0.75mm | UL 746 | PLC 0 | |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
flammability | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-2 |
0.75mm | UL 94 | V-2 | |
0.75mm | IEC 60695-11-10,-20 | V-2 | |
3.0mm | UL 94 | V-2 | |
1.5mm | IEC 60695-11-10,-20 | V-2 | |
0.38mm | UL 94 | V-2 | |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 825 °C |
UL flame retardant rating | 0.38mm | IEC 60695-11-10,-20 | V-2 |
Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 850 °C |
burning rate | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
Hot filament ignition temperature | 0.38mm | IEC 60695-2-13 | 825 °C |
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
burning rate | 0.380mm,Self-Extinguishing | ISO 3795 | 0.0 mm/min |
Burning wire flammability index | 0.38mm | IEC 60695-2-12 | 850 °C |
1.5mm | IEC 60695-2-12 | 960 °C | |
burning rate | 0.750mm,Self-Extinguishing | ISO 3795 | 0.0 mm/min |
Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 825 °C |
UL flame retardant rating | 1.5mm | UL 94 | V-2 |
Limiting Oxygen Index | ISO 4589-2 | 23 % | |
burning rate | 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min |
Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 825 °C |
physical property | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
viscosity number | ISO 307 | 145 cm³/g |
Thermal performance | Test Condition | Test Method | A SCHULMAN USA/6MV14 FR4 K1681 |
---|---|---|---|
RTI Str | 0.75mm | UL 746 | 110 °C |
RTI Elec | 0.38mm | UL 746 | 130 °C |
RTI Imp | 1.5mm | UL 746 | 100 °C |
RTI Elec | 3.0mm | UL 746 | 130 °C |
RTI Imp | 0.38mm | UL 746 | 75.0 °C |
3.0mm | UL 746 | 100 °C | |
RTI Elec | 0.75mm | UL 746 | 130 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 76.0 °C |
RTI Imp | 0.75mm | UL 746 | 90.0 °C |
ball-indentation hardness | 200°C | IEC 60695-10-2 | Pass |
vicat | -- | ISO 306/A50 | 217 °C |
RTI Str | 0.38mm | UL 746 | 100 °C |
1.5mm | UL 746 | 120 °C | |
vicat | -- | ISO 306/B50 | 202 °C |
RTI Str | 3.0mm | UL 746 | 120 °C |
RTI Elec | 1.5mm | UL 746 | 130 °C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/Bf | 186 °C |