Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-707K ZHANGZHOU CHIMEI
POLYLAC®
Office supplies,Lighting fixtures,Electronic field,Electrical field
High rigidity,High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-707K |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 116 |
| thermal performance | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-707K |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,退火 | ISO 75-2/A | 98.0 °C |
| 1.8MPa,未退火 | ASTM D648 | 85.0 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 83.0 °C | |
| 1.8MPa,退火 | ASTM D648 | 95.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.4E-05 cm/cm/°C |
| Vicat softening temperature | -- | ISO 306/B50 | 100 °C |
| -- | ASTM D15257 | 105 °C | |
| -- | ISO 306/A50 | 104 °C |
| mechanical properties | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-707K |
|---|---|---|---|
| Bending modulus | --5 | ASTM D790 | 2830 Mpa |
| --6 | ISO 178 | 2300 Mpa | |
| bending strength | --5 | ASTM D790 | 84.1 Mpa |
| --6 | ISO 178 | 79.0 Mpa | |
| elongation | 断裂4 | ASTM D638 | 20 % |
| 断裂 | ISO 527-2/50 | 30 % | |
| tensile strength | 屈服4 | ASTM D638 | 47.9 Mpa |
| 屈服 | ISO 527-2/50 | 50.0 Mpa | |
| 断裂 | ISO 527-2/50 | 36.0 Mpa |
| Physical properties | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-707K |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.7 g/10min |
| Melt Volume Flow Rate (MVR) | 220°C/10.0kg | ISO 1133 | 20.0 cm3/10min |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % |
| flammability | Test Condition | Test Method | ZHANGZHOU CHIMEI/PA-707K |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |