PBT 3216 JAPAN POLYPLASTIC
DURANEX® 
Laptop case
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodJAPAN POLYPLASTIC/3216
Surface Resistivity------3×1016 Ω
arc resistance*2---70 S
*2---250 V
Basic performanceTest ConditionTest MethodJAPAN POLYPLASTIC/3216
density---ASTM D-7921.54 ---
Mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/3216
bending strengthASTM D790/ISO 178166 kg/cm²(MPa)[Lb/in²]
tensile strength ---ASTM D-638112 Mpa
Flexural modulusASTM D790/ISO 1786080 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap缺口，---ASTM D-25658 J/m
Charpy Notched Impact StrengthASTM D256/ISO 17958 kg·cm/cm(J/M)ft·lb/in
Flexural modulus---ASTM D-7906080 Mpa
Impact strength of cantilever beam gap反缺口侧，---ASTM D-256440 J/m
elongation at breakASTM D638/ISO 5273.5 %
bending strength---ASTM D-790166 Mpa
tensile strength ASTM D638/ISO 527112 kg/cm²(MPa)[Lb/in²]
elongation at break---ASTM D-6383.5 %
Electrical performanceTest ConditionTest MethodJAPAN POLYPLASTIC/3216
Volume resistivity3mmtASTM D-2572×1016 Ω.cm
dielectric strength短时：3mmtASTM D-14920 MV/m
otherTest ConditionTest MethodJAPAN POLYPLASTIC/3216
characteristicGF15%
Physical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/3216
densityASTM D792/ISO 11831.54
Thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/3216
UL flame retardant rating---UL 94V-0 ---
Heat distortion temperature1.82MPa，HDTASTM D-648208 °C
HDTASTM D648/ISO 75208 ℃（℉）
Linear coefficient of thermal expansion------2-7 ×10-5/℃
ASTM D696/ISO 113592-7 mm/mm.℃