TPU A70E5040 HUNTSMAN GERMANY
IROGRAN®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | HUNTSMAN GERMANY/A70E5040 |
|---|---|---|---|
| 邵氏A,注塑 | ASTMD2240 | 75 | |
| 邵氏A,注塑 | ISO868 | 75 | |
| 邵氏D,注塑 | ISO868 | 25 | |
| 邵氏D,注塑 | ASTMD2240 | 25 |
| Mechanical properties | Test Condition | Test Method | HUNTSMAN GERMANY/A70E5040 |
|---|---|---|---|
| Abrasion2 | ISO4649 | 80 mm³ |
| physical property | Test Condition | Test Method | HUNTSMAN GERMANY/A70E5040 |
|---|---|---|---|
| Melt volume flow rate | 190°C/21.6kg | ISO1133 | 30.0 cm3/10min |
| Shrinkage rate | 2.5 % |
| elastomer | Test Condition | Test Method | HUNTSMAN GERMANY/A70E5040 |
|---|---|---|---|
| elongation | 断裂 | ASTMD412 | 650 % |
| Compression permanent deformation 2 | 23°C,24hr | ASTMD395 | 35 % |
| Tear strength 2 | ASTMD624 | 52.5 kN/m | |
| Compression permanent deformation 2 | 巴肖氏弹性 | ISO815 | 25 % |
| 70°C,24hr | ISO815 | 58 % | |
| Tensile stress 2 | 100%应变 | DIN53504 | 3.30 Mpa |
| 300%应变 | ASTMD412 | 6.55 Mpa | |
| elongation | 断裂 | DIN53504 | 650 % |
| Tensile stress 2 | 300%应变 | DIN53504 | 5.80 Mpa |
| Compression permanent deformation 2 | 23°C,24hr | ISO815 | 35 % |
| Tear strength 2 | ISO34-1 | 45 kN/m | |
| Tensile stress 2 | 100%应变 | ASTMD412 | 3.93 Mpa |
| tensile strength | 断裂 | ASTMD412 | 15.2 Mpa |
| Compression permanent deformation 2 | 70°C,24hr | ASTMD395 | 45 % |
| Tensile stress 2 | 断裂 | DIN53504 | 30.0 Mpa |
| Thermal performance | Test Condition | Test Method | HUNTSMAN GERMANY/A70E5040 |
|---|---|---|---|
| melting temperature | 125to190 °C |