PET FR515 DUPONT SHENZHEN
Rynite®
Fitness equipment、Automotive Applications
Glass fiber reinforced、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 20 kJ/m² |
| 23°C | ISO 179/1eU | 40 kJ/m² | |
| -30°C | ISO 179/1eU | 35 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| M计秤 | ISO 2039-2 | 88 |
| Electrical performance | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| Dissipation Factor | 100Hz | IEC 60250 | 9E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6800 Mpa | |
| bending strength | ISO 178 | 170 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
| Flexural modulus | ISO 178 | 5940 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 107 Mpa |
| flammability | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | IEC 60695-11-10,-20 | V-0 |
| 1.5mm | IEC 60695-11-10,-20 | 5VA | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | 5VA |
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| UL flame retardant rating | 0.9mm | UL 94 | V-0 |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| Ejection Temperature | 170 °C | ||
| Shrinkage rate | MD2 | ISO 294-4 | 0.50 % |
| TD2 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/FR515 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 254 °C | |
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1.2E-05 cm/cm/°C |
| TD：-- | ISO 11359-2 | 8.8E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 3.3E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.8E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 240 °C |
| vicat | ISO 306/B50 | 210 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |