PPO(PPE) PRL PPX-G20 Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX-G20 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C,3.18mm | ASTM D256 | 53 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1 | 6.3 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.3 kJ/m² |
| 23°C,3.18mm | ASTM D256 | 80 J/m |
| hardness | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX-G20 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 106 |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX-G20 |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 3.0 % |
| Flexural modulus | 3.17mm | ASTM D790 | 5170 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 93.1 MPa |
| Break,3.18mm | ASTM D638 | 93.1 MPa | |
| bending strength | 3.18mm | ASTM D790 | 138 MPa |
| Electrical performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX-G20 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX-G20 |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.20to0.50 % |
| melt mass-flow rate | 250°C/11.6kg | ASTM D1238 | 1.0to8.0 g/10min |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PPX-G20 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 138 °C |
| 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 132 °C | |
| vicat | ASTM D15252 | 143 °C |