Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM M140 CELANESE USA
CELCON®
currency
High mobility、No fill
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | CELANESE USA/M140 |
|---|---|---|---|
| Water absorption rate | Saturation,23℃ | ISO 62 | 0.75 % |
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 12 cm |
| Shrinkage rate | Across flow | ASTM D955 | 1.8 % |
| density | ASTM D792 | 1.41 g/cm | |
| Water absorption rate | Equilibrium,23℃,50%rh | ISO 62 | 0.2 % |
| Shrinkage rate | Across flow | ISO 294-4 | 1.7 % |
| flow | ISO 294-4 | 1.8 % | |
| flow | ASTM D955 | 2.2 % |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/M140 |
|---|---|---|---|
| tensile strength | Yield | ISO 527-2/1A/50 | 65 MPa |
| Yield,23℃ | ASTM D638 | 60.7 MPa | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 5.7 KJ/m |
| Tensile modulus | ISO 527-2/1A/1 | 94.5 MPa | |
| Flexural modulus | 23℃ | ISO 178 | 2640 MPa |
| Tensile creep modulus | 1HR | ISO 899-1 | 2350 MPa |
| 1000HR | ISO 899-1 | 1300 MPa | |
| tensile strength | Yield,-40℃ | ASTM D638 | 94.5 MPa |
| Thermal performance | Test Condition | Test Method | CELANESE USA/M140 |
|---|---|---|---|
| Linear coefficient of thermal expansion | flow | ISO 11359-2 | 0.00010 cm/cm/℃ |
| vicat | ISO 306/B50 | 161 ℃ | |
| Linear coefficient of thermal expansion | Transverse | ISO 11359-2 | 0.00010 cm/cm/℃ |
| Heat distortion temperature | 1.8MPa,Unannealed，HDT | ISO 75-2/A | 102 ℃ |
| 1.8MPa,Unannealed，HDT | ASTM D648 | 110 ℃ | |
| melting temperature | DSC | ISO 11357 | 166 ℃ |
| Heat distortion temperature | 0.45MPa,Unannealed，HDT | ISO 75-2/B | 156 ℃ |