Product Name
Brand Name
Usages
Properties
Certificates
PBT+PET POCAN® T 7391 POS151 900044 德国朗盛
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | <10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 5560 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | <10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| Supplementary Information | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| electrolytic corrosion | IEC 60426 | A1 | |
| ISO Shortcut | ISO 7792 | PBT+PET.GHLMR.09-160.GF45 |
| hardness | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| ISO 2039-1 | 250 MPa |
| Mechanical properties | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 1.9 % |
| Bending Strain | 23°C | 2.1 % | |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 160 MPa |
| Tensile creep modulus | 1hr | ISO 899-1 | 16500 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 16000 MPa |
| Flexural modulus | 23°C | ISO 178/A | 15500 MPa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 15000 MPa |
| bending strength | 23°C | ISO 178 | 260 MPa |
| Electrical performance | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| 23°C,1MHz | IEC 60250 | 4.20 | |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 28 kV/mm |
| 23°C,100Hz | IEC 60250 | 4.30 | |
| Volume resistivity | 23°C | IEC 60093 | >1.0E+15 ohms·cm |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.014 |
| flammability | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| MD:270°C,2.00mm2 | ISO 294-4 | 0.20 % | |
| density | 23°C | ISO 1183 | 1.69 g/cm³ |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| 降低的粘度 | ISO 1628 | 80.0 ml/g | |
| Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 0.80 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| Thermal performance | Test Condition | Test Method | 德国朗盛/POCAN® T 7391 POS151 900044 |
|---|---|---|---|
| BallPressure Test | 220°C | IEC 60695-10-2 | Pass |
| TemperatureIndex | 抗张强度 | IEC 60216 | 155 |
| thermal conductivity | 23°C | ISO 8302 | 0.27 W/m/K |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 225 °C |
| TemperatureIndex | 介电强度 | IEC 60216 | 155 |
| Hot deformation temperature (HDT) | 8.0MPa,未退火，HDT | ISO 75-2/C | 150 °C |
| melting temperature | ISO 11357-3 | 225to250 °C | |
| MD：23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C | |
| vicat | ISO 306/B120 | 210 °C | |
| Half Interval | --7 | IEC 60216 | 13.5 °C |
| --8 | IEC 60216 | 10.2 °C | |
| --9 | IEC 60216 | 10.2 °C | |
| TemperatureIndex | 拉伸冲击强度 | IEC 60216 | 150 |