PBT 5101G-30U TORAY JAPAN
Toraycon®
Automotive Applications,Electrical components
High impact resistance,Fast forming cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 65 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 60 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 6.70 CM |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| arc resistance | ASTM D495 | 130 S | |
| dielectric constant | 50Hz | ASTM D150 | 3.9 |
| Dielectric loss | 10，正切 | ASTM D150 | 0.02 |
| dielectric strength | ASTM D149 | 31 MV/m | |
| Dielectric loss | 50Hz，正切 | ASTM D150 | 0.002 |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 | |
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.90 |
| 23°C,1kHz | IEC 60250 | 3.70 | |
| Volume resistivity | IEC 60093 | 1E+17 ohms·cm | |
| arc resistance | IEC 60950 | 130 sec | |
| dielectric constant | 10 | ASTM D150 | 3.7 |
| Volume resistivity | ASTM D257 | 5.0 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 89 M | |
| coefficient of friction | 0.19 | ||
| Tensile modulus | 23°C | ISO 527-2 | 8500 Mpa |
| bending strength | 23℃ | ASTM D790 | 185 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 7.0 GPa |
| coefficient of friction | 对本身 | ASTM D1894 | 0.19 |
| Friction coefficient - vs. Metal | SuzukiMethod | 0.15 | |
| elongation | 23℃ | ASTM D638 | 5 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 205 Mpa |
| Flexural modulus | 23°C | ISO 178 | 8000 Mpa |
| tensile strength | 23℃ | ASTM D638 | 130 Mpa |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D256 | 145 J/m |
| coefficient of friction | 对金属 | ASTM D1894 | 0.15 |
| Impact strength of cantilever beam gap | 无缺口，23℃ | ASTM D256 | 85 KJ/m |
| tensile strength | 23°C | ISO 527-2 | 130 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Shrinkage rate | MD:3.00mm3 | 内部方法 | 0.40 % |
| Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5101G-30U |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，HDT | ASTM D648 | 225 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.82Mpa，HDT | ASTM D648 | 215 °C |
| Linear coefficient of thermal expansion | ASTM D696 | 2.5 | |
| UL flame retardant rating | UL 94 | HB |