PBT 5174G-R TORAY JAPAN
Toraycon®
Electrical applications、Electrical components
Flame retardant、High impact resistance、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO75-2/A | 207 °C | |
| Linear thermal expansion coefficient | MD：-30到100°C | ISO11359-2 | 5E-05 cm/cm/°C |
| Additional | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| 250°C,1.00mm | 内部方法 | 113 mm |
| Physical | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 0.90 % |
| MD:3.00mm4 | 0.40 % | ||
| Moisture Absorption | 23°C,24hr | ISO62 | 0.070 % |
| Mechanical Properties | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Tensile Strain | 断裂,23°C | ISO527-2 | 3.1 % |
| Flexural Modulus | 23°C | ISO178 | 6300 Mpa |
| Coefficient of Friction | 0.20 | ||
| Tensile Modulus | 23°C | ISO527-2 | 6600 Mpa |
| Tensile Stress | 屈服,23°C | 95.0 Mpa | |
| Flexural Stress | 23°C | ISO178 | 150 Mpa |
| Coefficient of Friction (vs.Metal) | SuzukiMethod | 0.16 |
| Impact Properties | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 57 kJ/m² |
| Flammability | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Flame Rating | 1.6mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Dielectric Constant | 23°C,1kHz | IEC60250 | 3.80 |
| 23°C,50Hz | 3.80 | ||
| Dissipation Factor? | 2E-03 | ||
| 23°C,1MHz | 0.020 |