Certificates
PC GN-3610ZL TEIJIN SHANGHAI
--
Industrial applications、Electrical/Electronic App、Electrical components
Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN SHANGHAI/GN-3610ZL |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 42 kJ/m² |
| Electrical performance | Test Condition | Test Method | TEIJIN SHANGHAI/GN-3610ZL |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Dielectric strength 3 | IEC60243-1 | 35 KV/mm | |
| CTI | IEC60112 | 175 V | |
| dielectric constant | 1MHz | IEC60250 | 3.20 |
| Dissipation Factor | 100Hz | IEC60250 | 1E-03 |
| dielectric constant | 100Hz | IEC60250 | 3.20 |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 1MHz | IEC60250 | 9E-03 |
| Mechanical properties | Test Condition | Test Method | TEIJIN SHANGHAI/GN-3610ZL |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 67.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/5 | 3.0 % |
| Bending modulus 2 | ISO178 | 3600 Mpa | |
| Bending stress 2 | ISO178 | 115 Mpa |
| flammability | Test Condition | Test Method | TEIJIN SHANGHAI/GN-3610ZL |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL94 | V-1 |
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 850 °C |
| Burning wire flammability index | 1.6mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| 1.6mm | IEC60695-2-13 | 850 °C | |
| UL flame retardant rating | 0.40mm | UL94 | V-2 |
| 1.6mm | UL94 | V-0 | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | TEIJIN SHANGHAI/GN-3610ZL |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.16 % |
| density | ISO1183 | 1.27 g/cm³ | |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.30to0.50 % |
| TD:4.00mm | 内部方法 | 0.40to0.60 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SHANGHAI/GN-3610ZL |
|---|---|---|---|
| TD | ISO11359-2 | 6E-05 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 138 °C | |
| vicat | ISO306/B50 | 140 °C | |
| RTI Elec | 1.5mm | UL746 | 80.0 °C |
| RTI Str | 1.5mm | UL746 | 80.0 °C |
| 1.8MPa,未退火 | ISO75-2/A | 134 °C | |
| RTI Imp | 1.5mm | UL746 | 80.0 °C |
| MD | ISO11359-2 | 4E-05 cm/cm/°C |