Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML-1103 TEIJIN JAPAN
PANLITE®
transparent、High rigidity、Thermal stability
transparent、High rigidity、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 141 °C |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 129 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | ISO306/B50 | 148 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ | |
| Heat Deflection Temperature | ASTM D648/ISO 75 | 141 ℃（℉） |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 % |
| MD:4.00mm | 0.50to0.70 % | ||
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Flexural Strength | ASTM D790/ISO 178 | 96.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile Stress | 断裂 | ISO527-2/50 | 59.0 Mpa |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 120 % | |
| Tensile Strength | 66.0 kg/cm²(MPa)[Lb/in²] | ||
| Tensile Modulus | ISO527-2/1 | 2400 Mpa | |
| Nominal Tensile Strain at Break | ISO527-2/50 | >50 % | |
| Tensile Modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | 6.0 % | ||
| Flexural Modulus | ISO178 | 2230 Mpa | |
| Tensile Stress | 屈服 | ISO527-2/50 | 61.0 Mpa |
| Tensile Strain | 6.0 % | ||
| Flexural Stress | ISO178 | 93.0 Mpa | |
| Flexural Modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] |
| Optical | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Transmittance | 3000µm | ASTMD1003 | 47.0 % |
| Other | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Remarks | 以上加工数据，为参考值.以生产厂商设备的实际状况而进行调整 |
| Impact Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak |
| Physical Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.20 % | |
| Modeling Shrinkage | ASTM D955 | 0.50-0.70 % |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/ML-1103 |
|---|---|---|---|
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω | |
| IEC60093 | >1.0E+15 ohms | ||
| Volume Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω.cm |