Phenolic Plenco 02000 (Compression) Plastics Engineering Co.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256 | 18.7 J/m | |
| Impact strength of cantilever beam gap | ASTM D256 | 17 J/m |
| hardness | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| Rockwell hardness | E计秤 | ASTM D785 | 90 |
| Mechanical properties | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 0.60 % |
| tensile strength | ASTM D638 | 51.0 MPa | |
| compressive strength | ASTM D695 | 212 MPa | |
| Flexural modulus | ASTM D790 | 8120 MPa | |
| Tensile modulus | ASTM D638 | 8600 MPa | |
| bending strength | ASTM D790 | 92.3 MPa |
| Electrical performance | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 3.2E+11 ohms·cm | |
| dielectric strength | ASTM D149 | 12 kV/mm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.052 |
| dielectric constant | 1MHz | ASTM D150 | 5.20 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | 132 sec |
| flammability | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| Limiting Oxygen Index | ASTM D2863 | 28 % |
| physical property | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.44 % |
| Water absorption rate | 24hr | ASTM D570 | 0.40 % |
| Apparent density | ASTM D1895 | 0.63 g/cm³ | |
| density | ASTM D792 | 1.39 g/cm³ |
| Thermal performance | Test Condition | Test Method | Plastics Engineering Co./Plenco 02000 (Compression) |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 176 °C |
| Continuous use temperature | ASTM D794 | 207 °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 5.9E-05 cm/cm/°C |
| thermal conductivity | 100°C | ASTMC177 | 0.39 W/m/K |