PA/MXD6 1032H BK MITSUBISHI ENGINEERING JAPAN
RENY™ 
Automotive sector、Electronic field、Electrical field
Glass fiber reinforced、Filler: Glass fiber reinf、60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1032H BK
Impact strength of simply supported beam without notch23°CISO 17954 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1032H BK
Tensile modulusISO 527-224700 Mpa
bending strengthISO 178429 Mpa
Tensile strain断裂ISO 527-21.4 %
Flexural modulusISO 17823200 Mpa
tensile strength 断裂ISO 527-2249 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1032H BK
dielectric strength1.00mmIEC 60243-126 KV/mm
Volume resistivityIEC 600932E+15 ohms·cm
relative permittivity100HzIEC 60250--
Dissipation Factor100HzIEC 60250--
dielectric strength2.00mmIEC 60243-120 KV/mm
relative permittivity1MHzIEC 60250--
Surface ResistivityIEC 600932E+14 ohms
Dissipation Factor1MHzIEC 60250--
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1032H BK
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1032H BK
Shrinkage rate0.40 %
Melt volume flow rate275°C/2.16kgISO 11335.30 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.90 %
饱和,23°CISO 620.11 %
melt mass-flow rate275°C/2.16kgISO 11339.4 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/1032H BK
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B237 °C
1.8MPa,未退火，HDTISO 75-2/A230 °C
Linear coefficient of thermal expansionMDISO 11359-21E-05 cm/cm/°C
TDISO 11359-24E-05 cm/cm/°C