Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT CE2055 NC010 DUPONT USA
Cristin®
Automotive sector、Fitness equipment、Lighting applications
Flame retardant、high strength、Conductive
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/CE2055 NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa退火 | ISO75-2/B | 184 °C |
| 0.45MPa未退火 | ISO75-2/Bf | 150 °C | |
| 1.80MPa退火 | ISO75-2/A | 73 °C | |
| Vicat Softening Temperature | 熔融温度 | ISO11357-3 | 225 °C |
| ISO306/B50 | 175 °C | ||
| Heat Deflection Temperature | 1.80MPa退火 | ISO75-2/Af | 55 °C |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/CE2055 NC010 |
|---|---|---|---|
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 13 % |
| Flexural Strength | ISO178 | 82.0 Mpa | |
| ASTM D790/ISO 178 | 82 kg/cm²(MPa)[Lb/in²] | ||
| Tensile Modulus | 0.00 mm, 23 ℃, Injection Molded | ISO 527-1, -2 | 2600 MPa |
| Tensile Strength | 23°C | ISO527-2 | 60.0 Mpa |
| Tensile Modulus | 2600 Mpa | ||
| Notched Izod Impact Strength | ISO180/1A | 3.9 kJ/m² | |
| Tensile Modulus | ASTM D638/ISO 527 | 2600 kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | 0.00 mm, 23 ℃, 0.0 % | ISO 178 | 82 MPa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 3.5 kJ/m² |
| Physical | Test Condition | Test Method | DUPONT USA/CE2055 NC010 |
|---|---|---|---|
| Modeling Shrinkage | TD2.0mm | ISO294-4 | 2.00 % |
| MD2.0mm | 1.80 % |
| Other | Test Condition | Test Method | DUPONT USA/CE2055 NC010 |
|---|---|---|---|
| characteristic | 低粘度 经润滑 |
| Physical Properties | Test Condition | Test Method | DUPONT USA/CE2055 NC010 |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.31 |
| Processing | Test Condition | Test Method | DUPONT USA/CE2055 NC010 |
|---|---|---|---|
| Mold Temperature | 30-130 °C |