Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5010G-30 BK2 MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Bottle cap、Fitness equipment、Automotive sector、Electronic field、Electrical field
Glass fiber reinforced、30% glass fiber reinforce、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 BK2 |
|---|---|---|---|
| Stretching length | ASTM D638 | 4.5 % | |
| Flexural modulus | ASTM D790 | 7.18 GPa | |
| Impact strength of cantilever beam gap | 3.2mm | ASTM D256 | 111 J/m |
| coefficient of friction | ASTM D1894 | 0.15 | |
| bending strength | ASTM D790 | 179.5 Mpa | |
| Rockwell hardness | ASTM D785 | 120 R | |
| tensile strength | ASTM D638 | 128.5 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 BK2 |
|---|---|---|---|
| arc resistance | ASTM D495 | 125 S | |
| Dielectric loss | 10，正切 | ASTM D150 | 0.016 |
| dielectric constant | 10 | ASTM D150 | 30 Pf/m |
| dielectric strength | ASTM D149 | 24 KV/mm | |
| Volume resistivity | ASTM D257 | 10 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 BK2 |
|---|---|---|---|
| Shrinkage rate | 平行方向 | 0.2 % | |
| filler content | 30 wt% | ||
| Shrinkage rate | 垂直方向 | 0.8 % | |
| Water absorption rate | 23℃,24hr | ASTM D570 | 0.08 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 BK2 |
|---|---|---|---|
| specific heat | 0.5 | ||
| Heat distortion temperature | 0.45MPa，HDT | ASTM D648 | 220 °C |
| 1.86Mpa，HDT | ASTM D648 | 210 °C | |
| melting temperature | DSC法 | 224 °C | |
| Linear coefficient of thermal expansion | 3 | ||
| UL flame retardant rating | UL 94 | HB |